让新材料造福人类生活
Advanced Materials, Better Lives.
三代核电站电缆用低烟无卤非核级材料
THIRD-GENERATION NUCLEAR POWER PLANT CABLE LSZH NON-NUCLEAR-GRADE MATERIALS
产品列表 PRODUCT LIST
| 产品编号 Product No. | 产品名称 Product Name | 产品牌号 Model | 特点及用途 Features |
|---|---|---|---|
| H014 | 核电站电缆专用辐照交联绝缘料 Irradiation cross-linked insulation compound for nuclear plant cables | NPS-1000E(B) | 60年，非核级，辐照交联、内绝缘 60 years; non-nuclear-grade; irradiation cross-linked; inner insulation |
| H015 | 核电站电缆专用辐照交联低烟无卤电缆料 Irradiation cross-linked LSZH cable compound for nuclear plant cables | NPS-1000ES(B) | 60年，非核级，辐照交联、外绝缘 60 years; non-nuclear-grade; irradiation cross-linked; outer insulation |
| H016 | 核电站类电缆专用辐照交联低烟无卤护套料 Irradiation cross-linked LSZH sheathing compound for nuclear plant cables | NPS-2000E(B) | 60年，非核级，辐照交联、护套 60 years; non-nuclear-grade; irradiation cross-linked; sheath |
| H017 | 核电站电缆专用热塑性低烟无卤护套料 Thermoplastic LSZH sheathing compound for nuclear plant cables | NPS-6000 | 60年，非核级，热塑性、护套 60 years; non-nuclear-grade; thermoplastic; sheath |
产品性能 PRODUCT CHARACTERISTICS
| 性能 Properties | 单位 Unit | NPS-1000E(B) H014 | NPS-1000ES(B) H015 | NPS-2000E(B) H016 | NPS-6000 H017 | 测试方法 Test methods |
|---|---|---|---|---|---|---|
| 密度 Density | g/cm³ | 0.94 | 1.59 | 1.48 | 1.49 | GB/T 1033-2008 ISO 1183-1:2012 |
| 拉伸强度 Tensile strength | MPa | 16.9 | 11.8 | 12.0 | 14.5 | GB/T 1040-2018 ISO 527:2012 |
| 断裂伸长率 Elongation at break | % | 570 | 260 | 170 | 205 | |
| 老化性能 Aging property | ℃×h | 135×240 | 135×240 | 135×240 | 110×240 | GB/T 2951.12-2008 IEC 60811-401-2012 |
| 拉伸强度变化率 Variation of tensile strength | % | +3 | +12 | +11 | +11 | |
| 断裂伸长率变化率 Variation of elongation at break | % | -4 | -10 | -9 | -13 | |
| 热延伸(0.2MPa) Hot set test | ℃×min | 200×15 | 200×15 | 200×15 | — | GB/T 2951.21-2008 IEC 60811-507-2012 |
| 负荷下伸长率 Elongation under load | % | 100 | 35 | 15 | — | |
| 冷却后永久变形率 Permanent elongation after cooling | % | 5 | 5 | 0 | — | |
| 低温冲击脆化温度 Low temperature brittleness | ℃ | -40 | -35 | -35 | -35 | GB/T 5470-2008 ISO 974:2000 |
| 耐IRM902油试验 Mineral oil resistance | ℃×h | — | — | 100×24 | 70×4 | GB/T 2951.12-2008 IEC60811-404-2012 |
| 拉伸强度变化率 Variation of tensile strength | % | — | — | -26 | -20 | |
| 断裂伸长率变化率 Variation of elongation at break | % | — | — | +8 | +15 | |
| 浸水试验 Water immersion test | ℃×h | — | 70×168 | 70×168 | 70×168 | prEN50363 2005 |
| 拉伸强度变化率 Variation of tensile strength | % | — | -8 | -6 | -8 | |
| 断裂伸长率变化率 Variation of elongation at break | % | — | -20 | -22 | -14 | |
| 体积电阻率(20℃) Volume resistivity | Ω·cm | 3.6×10¹⁶ | 2.5×10¹⁴ | 1.1×10¹⁴ | 3.1×10¹⁴ | GB/T 31838.2-2019 IEC62631-3-1:2016 |
| 体积电阻率(90℃) Volume resistivity | Ω·cm | 1.1×10¹⁵ | 3.2×10¹³ | 4.2×10¹² | 3.6×10¹² | GB/T 31838.7-2021 IEC62631-3-4:2019 |
| 介电强度(20℃) Dielectric strength | MV/m | 30 | 29 | 26 | 28 | GB/T 1408.1-2006 IEC 60243-1:2013 |
| 烟密度 Smoke density | — | — | — | — | — | GB 8323-2008 ISO 5659:2012 |
| 无焰 Non-flame | — | — | 256 | 235 | 249 | |
| 有焰 Flame | — | — | 30 | 50 | 58 | |
| 卤酸气体含量 Content of halogen acid gas | mg/g | 0 | 0 | 0 | 0 | GB/T 17650.1-2021 IEC60754-1:2019 |
| HF含量 Content of HF | % | 0 | 0 | 0 | 0 | IEC 60684-2:2021 |
| pH | — | 4.9 | 4.6 | 5.4 | 5.6 | GB/T 17650.2-2021 IEC60754-2:2019 |
| 电导率 Electrical conductivity | μ·s/mm | 1.0 | 1.3 | 1.1 | 1.2 | |
| 氧指数(20℃) Oxygen index | % | — | 30 | 33 | 35 | GB/T 2406-2009 ISO 4589-2:1996 |
| 毒性指数 Toxicity index | — | 1.0 | 0.7 | 1.0 | 1.0 | Def Stan 02-713 |
| 寿命评定试验(90℃) Thermal endurance properties test | 年 years | ≥60 | ≥60 | ≥60 | ≥60 | GB/T 11026.1-2016 IEC 60216-1:2013 |